Kimya – High Impact PLA – Black

$44.95

-

The 3D PLA-HI filament has been formulated to quadruple its impact resistance compared to PLA-S.

  • EASY TO PRINT
  • RESISTANCE TO IMPACT
  • NO ODOR
  • BIOSOURCED MATTER

PRINT SETTINGS:

  • PRINT SPEED : 50 mm/s
  • EXTRUSION TEMPERATURE : 200°C
  • PLATFORM TEMPERATURE : 60°C
Clear

SKU: N/A Categories: , , ,

Description

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.21 g/cm3
Moisture rate INS-6711 < 1 %
Melt flow index (MFI) ISO 1133-1 (@210°C – 2,16 kg) 5.7 g/10min
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min – 20-220°C) 60 °C
Melting Temperature (Tm) ISO 11357-1 DSC (10°C/min – 20-220°C) 156 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 50 mm/s
Infill 100% – rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 200°C
Bed T° 60°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
MECHANICAL PROPERTIES Tensile modulus ISO 527-2/5A/50 2,491 MPa
Tensile Strength ISO 527-2/5A/50 43 MPa
Tensile strain at strength ISO 527-2/5A/50 2 %
Tensile Stress at Break ISO 527-2/5A/50 22.9 MPa
Tensile strain at break ISO 527-2/5A/50 4.2 %
Flexural modulus ISO 178 2,097 MPa
Flexural stress at conventional deflection (3,5% strain)* ISO 178 62.8 MPa
Charpy impact resistance ISO 179-1/1eA 16.5 kJ/m²
Shore Hardness ISO 868 76,8D
Note 1 *According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values – Properties can be influenced by production conditions.

Created on 15/01/2018 – Revised on 29/07/2019.